    Chemical Cross-Linkable PE Overhead Insulation Black Compound (≤10KV) ...
    型号:0

    参考价:¥

    说明:如您对该产品感兴趣,请在此输入您的手机号将本产品的地址 发送至您手机上。

    Product description 产品描述
    Chemical cross-linkable PE insulation black compound for power cables which regard advanced LDPE resin as the main material, add antioxidant, cross-linking agent and other accessory additives, is manufactured by advanced closed extruder. It has excellent extrusion property and physical property, impurity content is controlled within limits. This product is mainly used for the insulation of medium-low voltage cross-linking overhead cables. Working temperature is 90℃.It is applicable for 10KV and below cross-linking cables.
    电力电缆用黑色可化学交联聚乙烯绝缘料是以优质低密度聚乙烯树脂为主要原德赢vwin客户端下载,加入抗氧剂、交联剂等配合剂,采用先进的封闭式混炼装置加工而成,它兼有良好的挤出性能和物理性能,杂质含量符合要求,专用于生产中、低压交联架空电缆绝缘,长期工作温度为90℃,本产品适用于10KV及以下交联电线电缆。
     
    Processing Indicator 加工工艺
    Recommend to process with the PE extruder. 建议使用聚乙烯专用挤出机进行加工。


    Model
    牌号
    Machine Barrel Temperature
    机筒温度
    Molding Temperature
    机头温度
    YJW-10
    100-115℃
    110-115℃

    Physical and Electrical Properties 物理和电气性能
    Item
    试验项目
    Unit
    单位
    Technical requirements
    技术要求
    Tensile Strength
    拉伸强度
    MPa
    ≥13.0
    Elongation at Break
    断裂伸长率
    %
    ≥300
    Brittle Temperature with Low Temperature
    低温脆化温度
    -76
    20℃Volume Resistivity
    20℃体积电阻率
    Ω·m
    ≥1.0×1013
    20℃Dielectric Strength,50Hz
    20℃介电强度, 50Hz
    MV/m
    ≥22.0
    20℃Dielectric Dissipation Factor,50Hz
    20℃介质损耗因数, 50Hz
    ---
    ≤0.001
    Resistance to Environmental Stress Cracking F0
    耐环境应力开裂F0
    h
    ≥1000
    Air Aging Condition
    热空气老化条件
    135℃×168h
    Tensile Strength Variation After Aging
    拉伸强度变化率
    %
    ±20
    Elongation Variation After Aging
    断裂伸长变化率
    %
    ±20
    Artificial Weathering Aging
    人工气候老化0-1008h
    Tensile Strength Variation After Aging
    拉伸强度变化率
    %
    ±30
    Elongation Variation After Aging
    断裂伸长率变化率
    %
    ±30
    Artificial Weathering Aging
    人工气候老化504-1008h
    Tensile Strength Variation After Aging
    拉伸强度变化率
    %
    ±30
    Elongation Variation After Aging
    断裂伸长率变化率
    %
    ±30
    Hot Set Test Condition
    热延伸试验条件
    200℃×0.2MPa×15min
    Hot Elongation
    负荷下伸长率
    %
    ≤80
    Permanent Deformation After Cooling
    冷却后永久形变
    %
    ≤5